封面: Cu-TCPP和Cu2O组成的有机/无机杂化单分散球形电催化剂,其在碱性电解质中(–1.0 V vs. RHE)电还原二氧化碳产C2产物法拉第效率达到62.3%,电流密度达到83.4 mA·cm-2。(文献号2303271)
扫描或识别二维码,免费查看、下载文献的PDF全文。
中国化学会电化学专业委员会. 电化学十大科学问题[J]. 电化学(中英文), 2024, 30(1): 2024121.Chinese Society of Electrochemistry. The Top Ten Scientific Questions in Electrochemistry[J]. Journal of Electrochemistry, 2024, 30(1): 2024121.DOI: 10.61558/2993-074X.3444
马海斌, 周晓延, 李嘉艺, 程洪飞, 马吉伟. 用于促进碱性介质中析氢反应动力学的异质结构电催化剂的合理设计[J]. 电化学(中英文), 2024, 30(1): 2305101.
Hai-Bin Ma, Xiao-Yan Zhou, Jia-Yi Li, Hong-Fei Cheng, Ji-Wei Ma. Rational Design of Heterostructured Nanomaterials for Accelerating Electrocatalytic Hydrogen Evolution Reaction Kinetics in Alkaline Media[J]. Journal of Electrochemistry, 2024, 30(1): 2305101.
DOI: 10.13208/j.electrochem.2305101
Owing to the merits of high energy density, as well as clean and sustainable properties, hydrogen has been deemed to be a prominent alternative energy to traditional fossil fuels. Electrocatalytic hydrogen evolution reaction (HER) has been considered to be mostly promising for achieving green hydrogen production, and has been widely studied in acidic and alkaline solutions. In particular, HER in alkaline media has high potential to achieve large-scale hydrogen production because of the increased durability of electrode materials. However, for the currently most prominent catalyst Pt, its HER kinetics in an alkaline solution is generally 2-3 orders lower than that occurring in an acidic solution because of the low H+ concentration in alkaline electrolytes. Fortunately, construction of heterostructured electrocatalysts has proved to be an efficient strategy for boosting alkaline HER kinetics because of their various structural merits. The synergistic effect is a unique characteristic of heterostructures, which means that one functional active site serves as a promoter for water dissociation and another one takes a charge of moderate hydrogen adsorption, thus synergistically improving HER performance. In addition, each building block of the heterostructures is tunable, providing more flexibility and chances to construct optimal catalysts. Furthermore, due to the presence of Fermi energy difference between the two components at the interface, the electronic structure of each component could possibly be rationally modulated, thus much enhanced HER performance in alkaline electrolyte can be achieved. With a deeper understanding of on nanoscience and rapid development of nanotechnology, more sophisticated alternative designing strategies have been explored for constructing high-performance heterostructured electrocatalysts. This review presents an outline of the latest development of heterostructured catalysts toward alkaline HER and the rational design principles for constructing interfacial heterostructures to accelerate alkaline HER kinetics. The basic reaction pathways of HER in alkaline media are first described, and then emerging efficient strategies to promote alkaline HER kinetics, including synergistic effect, strain effect, electronic interaction, phase engineering, and architecture engineering. Finally, current existing challenges and research opportunities that deserve further investigation are proposed for the consideration of novel heterostructures towards practical applications.
万紫轩, Aidar Kuchkaev, Dmitry Yakhvarov, 康雄武. 单分散Cu-TCPP/Cu2O杂化微球:一种具有优异电还原CO2产C2性能的级联电催化剂[J]. 电化学(中英文), 2024, 30(1): 2303271.Zi-Xuan Wan, Aidar Kuchkaev, Dmitry Yakhvarov, Xiong-Wu Kang. Monodispersed Cu-TCPP/Cu2O Hybrid Microspheres: A Superior Cascade Electrocatalyst toward CO2 Reduction to C2 Products[J]. Journal of Electrochemistry, 2024, 30(1): 2303271.
DOI: 10.13208/j.electrochem.2303271
The electrochemical conversion of carbon dioxide (CO2) into valuable chemicals is a feasible way to mitigate the negative impacts of overmuch CO2 emissions. Porphyrin-based metal organic frameworks (MOFs) are expected to be used for selective and efficient electrochemical CO2 reduction (ECR) with porous structure and ordered active sites. Herein, we report the synthesis of a monodispersed and spherical organic/inorganic hybrid Cu-TCPP@Cu2O electrocatalyst composed of Cu-TCPP (TCPP=tetrakis (4-carboxyphenyl) porphyrin) and Cu2O, where TCPP plays significant roles in regulating the morphology. In-situ formed Cu during ECR process in combination with Cu-TCPP (Cu-TCPP@Cu) can suppress hydrogen evolution, enrich CO intermediate and promote C-C coupling toward C2 products. The Cu-TCPP@Cu supported on porous carbon (PC) showed ultrafine Cu nanoclusters on PC, and displayed high ECR activity and selectivity toward C2 products, with a C2 faradaic efficiency of 62.3% at -1.0 V versus the reversible hydrogen electrode and a C2 partial current density of 83.4 mA·cm-2, which is 7.6 times and 13.1 times those of pure Cu2O and TCPP, respectively. The morphology and hybrid structure of the catalyst were studied to improve the selectivity of ECR to produce C2 products, which provides a new idea for the design of high-performance ECR catalyst.
汤亚飞, 武安祺, 韩贝贝, 刘华, 包善军, 林王林, 陈铭, 官万兵, Subhash C. Singhal. 以掺氢天然气为燃料直接内重整固体氧化物电池堆的稳定性[J]. 电化学(中英文), 2024, 30(1): 2314001.Ya-Fei Tang, An-Qi Wu, Bei-Bei Han, Hua Liu, Shan-Jun Bao, Wang-Lin Lin, Ming Chen, Wan-Bing Guan, Subhash C. Singhal. Stability of a Solid Oxide Cell Stack under Direct Internal-Reforming of Hydrogen-Blended Methane[J]. Journal of Electrochemistry, 2024, 30(1): 2314001. DOI: 10.61558/2993-074X.3430
In this work, the long-term stability and degradation mechanism of a direct internal-reforming solid oxide fuel cell stack (IR-SOFC stack) using hydrogen-blended methane steam reforming were investigated. An overall degradation rate of 2.3%·kh-1 was found after the stack was operated for 3000 hours, indicating a good long-term stability. However, the voltages of the two cells in the stack were increased at the rates of 3.38 mV·kh-1 and 3.78 mV·kh-1, while the area specific resistances of the three metal interconnects in the stack were increased to 0.276 Ω·cm2, 0.254 Ω·cm2 and 0.249 Ω·cm2. The degradation of the stack might be caused by segregation of chromium on the surface of metal interconnects and the formation of SrCrO4 insulating phase in the current collecting layer of the cathode, which result in an increase in the interfacial resistance and a decrease in the stack performance. The long-term performance of a flat-tube IR-SOFC stack could be further improved by suitably coating the metal interconnect surface. This work provides theoretical and experimental guideline for the application of hydrogen-blended methane steam reforming in flat-tube IR-SOFC stacks.