SCI论文中如何来描述SAXS实验结果？

相关内容链接：

1. 如何非常详细地描述SAXS的实验结果？

举例：

The SAXS pattern of the -extracted PMO-SBA-16 shows three well-resolved peaks at very small scattering angles, with interplanar d spacings of 12.8, 9.03, and 7.38 nm. These three peaks can be indexable as (110), (200), and (211) reflections of the body-centered 3D cubic space group (Im3m), similar to that reported for the silica-based mesoporous counterpart SBA-16. The unit cell parameter of the cubic lattice is as large as 18.1 nm. This is the first large-pore PMO material that exhibits such a highly ordered 3D mesostructure. By contrast, the SAXS pattern of the -extracted control sample F127 blank prepared in the absence of K₂SO₄ reveals the formation of amorphous gel.

参考文献 :, 2003, 2692-2693

提炼语言模板：

定性分析结果

观察到的结果：The SAXS pattern of the 样品名称 shows three well-resolved peaks at very small scattering angles, with interplanar d spacings of 面间距 nm.

对结果进行分析：These three peaks can be indexable as 晶面指数 reflections of the 晶体结构类型, similar to that reported for the 已报道的结果. 

定量分析结果

晶胞参数：The unit cell parameter of the cubic lattice is as large as __.

对比讨论

By contrast, the SAXS pattern of the 对比样品 prepared 制备条件 reveals the formation of amorphous gel.

备注：有关SAXS的基本原理以及数据分析，我们后面会结合实例对其进行分析，敬请期待！

2. 不同文章中描写XPS结果可能详略不一，下面总结一些比较常见的写法供大家参考。

注：蓝色字体部分即为句型模板。

A. LP-FDU-12 materials synthesized at low temperatures were first examined by X-ray diffraction (XRD) and further confirmed by the small-angle X-ray scattering (SAXS) method.The XRD pattern of S-17-100 shows six well-resolved diffraction peaks (SI). A typical SAXS pattern of sample S-17-100 (Figure 1a) also exhibits six peaks, which can be exactly indexed to the 111, 220,311, 331, 333, and 442 reflections of a fcc structure (Fm3m). The cell parameter is calculated to be 34.6 nm (33.0 nm from XRD). 

Ref.: J. Am. Chem. Soc., 2005, 127 (31),pp 10794–10795

B. The small-angle X-ray scattering (SAXS) patterns of as-made FDU-16 clearly show three well-resolved diffraction peaks with q values of 0.47, 0.64, and 0.80 nm^-1(Figure 1a). Four additional diffraction peaks at q values of 0.88, 1.04, 1.12, and 1.22 nm^-1 can also be detected. The q-value ratios of these peaks are exactly1:√2:√3:√4:√5:√6:√7 and canbe indexed as 110, 200,211, 220, 310, 222, and 321 Bragg reflections, respectively, associated with the body-centered cubic Im3̄m symmetry.

 Ref.: Chem. Mater., 2006, 18 (18),pp 4447–4464

C. The bulk structure of the mesoporous silica prepared with 1 as template via the nanocasting technique was characterized by small-angle X-ray scattering (SAXS). SAXS has turned out to be a powerful technique with which to investigate the structure of two-phase systems, (i.e.,nanostructure materials that can be supposed to be composed of two domains ofconstant electron density). The SAXS diffractogram of the present sample is shown in Figure 2. It exhibits a significantly main peak at s ≈ 0.20 nm,^-1 which corresponds to the packing of the wormlike pores into a certain distorted 3D alignment. The position of th epeak is related to a length scale of approximately 5 nm, the averaged pore-to-pore distance, in good agreement with the TEM observation.

Ref.: Nano Letters, 2004, 4 (3), pp 477–481

当SAXS作为一个辅助的表征手段来印证前面的表征结果时，也可以写得很简单

D. Small-angle X-ray scattering (SAXS; see the Supporting Information) reveals four well-resolved reflections, further confirming a highly ordered hexagonal mesostructure. 

E.  Small-angle X-ray scattering experiments confirmed the presence of two kinds of cubic structures (CD and CP). 

Ref.: Langmuir, 2001, 17, 3917–3922

---

研之成理面向所有感兴趣的朋友征集专栏作家，主要包括专业软件（比如Digital Micrograph, TIA, Photoshop，Chemoffice，Material studio等）和基础知识（XRD结构精修，热分析，核磁，程序升温实验，同步辐射，质谱，AFM，STM）的分享，以及相关领域最新文献赏析。目前，由于小编人数有限，总结的周期会比较长，如果有更加专业的人来分担一部分的话，应该可以让大家更快更好地学到更多内容。

欢迎愿意分享的朋友联系我们：邹主编（QQ：337472528）或者陈主编（QQ：708274），谢谢！

最后，真诚地希望大家能够在这个平台上展示自己，将自己的思想传递给更多的人。

---

---

为方便研友们进行学术讨论，研之成理也开创了自己的QQ群，1号群：已满；2号群：已满；3号群：585629919。欢迎大家加入进行激烈的学术讨论！

本文版权属于研之成理，转载请通过QQ联系我们，未经许可请勿盗版，谢谢！

长按下图识别图中二维码或者搜索微信号rationalscience，轻松关注我们，谢谢！